SikaGrout®-9610

Shrinkage-compensated and high-performance cementitious grout with advanced nano-engineered technology for offshore, marine and civil infrastructure applications

SikaGrout®-9610 is a ready-to-use, shrinkage-compensated, homogeneous, flowable, and pumpable high-performance cementitious (HPC) grout for offshore, marine and civil infrastrucres. Incorporating advanced nano-engineered binder technology with a blend of Portland, pozzolan, and special cements, SikaGrout®-9610 achieves superior technical performance and exceptional rheological properties. Anti-washout properties and low water permeability make this grout particularly effective for offshore and marine structure grouting and other demanding applications involving narrow constrictions and complex filling needs.

  • Good flowability
  • High early strength
  • Shrinkage compensated
  • No segregation or bleeding to ensure consistent final physical performance
  • Wide range of application between 2 to 40oC without special precautions
  • Volume stable
 
Contact

Usage

SikaGrout®-9610 has been especially formulated for large scale, pump applications.
  • Grouting of pile-sleeve connections of offshore jacket foundations
  • Grouting of bolted monopile/transition piece skirt annuli  
  • Grouting of mooring and berthing dolphins for marine terminals
  • Grouting of piled pier and jetty structures
  • General purpose grouting for civil infrastructures
Contact the Technical Department of your local Sika office regarding any application required not mentioned here  

Advantages

  • Good flowability
  • High early strength
  • Shrinkage compensated
  • No segregation or bleeding to ensure consistent final physical performance
  • Wide range of application between 2 to 40oC without special precautions
  • Volume stable
 

Packaging

SikaGrout®-9610 is supplied in special 25 kg bags and 500, 1000, 1500 kg big bags

Product Details

Product Information

Composition

SikaGrout®-9610 has a C3A content of approximately 3.1-3.4% by mass of dry powder

Shelf life

12 months from date of production

Storage conditions

Product must be stored in original, unopened and undamaged sealed packaging in dry conditions away from direct sunlight and heat, not exceeding 40 oC. When stored under high temperature and high humidity conditions, the shelf life may be reduced.

Density

2.27 - 2.33 ton/m3

(EN 12390-7)

Total chloride ion content

< 0.01 %
Technical Information

Compressive strength

Age

N/mm2

1 day

> 35

3 days

> 55

7 days

> 60

28 days

> 80

91 days

> 85

40 x 40 x 160 mm prisms, at 25 oC

Age

At 25 oC (N/mm2)

At 30 oC (N/mm2)

1 day

> 35

> 40

3 days

> 55

> 65

7 days

> 60

> 70

28 days

> 80

> 85

91 days

> 85

> 90

50 mm & 75 mm cubes results

Exposure classes:

X0, XC1-4, XS1-3, XD1-3, XF1, XA1-3

Modulus of elasticity in compression

> 30.000 N/mm2

(EN 12390-13)

Poisson's ratio:

0.20

(ASTM C469)

Flexural-strength

> 11.0 N/mm2

(EN 1015-11)

Tensile strength

> 6.0 N/mm2

(ASTM C307)

Shrinkage

< 0.015 %

at 91 days

Bleeding

0 % (No bleeding)

(ASTM C940)

Application

Application Information

Mixing ratio

13.8 to 15.3 % water / powder ratio

Layer thickness

25 - 600 mm

Material temperature

2 °C min. / +40 °C max.

Ambient air temperature

2 °C min. / +40 °C max.

Substrate temperature

2 °C min. / +40 °C max.

Pot Life

3 hours

Flowability

Flow table

270 - 330 mm

Flow channel

> 550

Setting time

Initial

Final

7 hours

9.5 hours
Consumption

Consumption

Approximately 500 liters per ton material
Application steps

NOTES ON INSTALLATION

  • SikaGrout®-9610 has been especially formulated for use in specific applications. As such SikaGrout®-9610 should be installed by experienced fully trained contractors.

  • Sands or other products that could affect the products properties must not be added.

EQUIPMENT

Mixer type

Paddle mixer

Mixing time

Approximately 5 minutes

Application method

One continuous pour

MIXING

SikaGrout®-9610 must be mixed using suitable grout mixing equipment combined with agitator for continuous large volume mixing. Volume capacity of equipment must be applicable to the volume of material being mixed for a continuous operation. Equipment trials must be considered to ensure product can be mixed satisfactory before full project application. Put most of the water required in the mixer and add slowly the grout material.

 

Mix until a homogeneous mortar (2 to 3 minutes), add the remaining water and continue mixing for at least another 2 minutes until the required fluid or flowable consistency is obtained. Mix with potable water only. Do not add more water than the maximum specified.

CLEANING OF EQUIPMENT

Tools and spillages can be cleaned with water while SikaGrout®-9610 is still uncured. Once hardened, the material can only be removed mechanically.